Researchers develop high-performance heterojunction pn diodes
The date of：
2024-12-30
viewed:
0
A research team has developed high-performance diamond/ε-Ga2O3 heterojunction pn diodes based on ultrawide bandgap semiconductors, achieving breakdown voltages exceeding 3 kV. This work was published in Nano Letters.The research was led by Prof. Ye Jichun from the Ningbo Institute of Materials Technology and Engineering (NIMTE) of the Chinese Academy of Sciences (CAS), together with researchers from Zhengzhou University, Nanjing University, Harbin Institute of Technology, and Yongjiang Laboratory.Ultrawide bandgap semiconductors including Ga2O3 and diamond demonstrate notable potential for high-power applications due to their ultrawide bandgap, high breakdown field, radiation resistance, and carrier mobility. Bipolar devices, such as pn diodes and bipolar junction transistors, hold promising potential in the high-power electronics industry due to their ability to withstand reverse voltage currents.However, effective bipolar doping in ultrawide bandgap semiconductors is limited by the substantial ionization energies of dopants. To overcome this bottleneck, the researchers have proposed a heterojunction strategy. This approach integrates p-type diamond with n-type ε-Ga2O3 for fabricating power pn diodes.The heteroepitaxial n-type ε-Ga2O3 film was grown on the p-type diamond single-crystal substrate by coordinating multi-domains and confining the crystallization pathway. This process alleviates lattice mismatch. The heterojunction interface between ε-Ga2O3 and diamond is atomically sharp without observable interfacial element diffusion, enabling highly efficient rectification and low reverse leakage current in the heterojunction diodes.Compared with previously reported diamond-based diodes, the fabricated diamond/ε-Ga2O3 heterojunction diode exhibits notable rectifying characteristics, with an on−off ratio exceeding 108. It achieves a maximum breakdown voltage surpassing 3,000 V, even without edge termination.Additionally, a thermal boundary conductance of up to 64 MW/m2·K at 500 K was achieved, demonstrating the thermal management capability of the diamond/ε-Ga2O3 heterojunction diode.This study introduces an innovative methodology for fabricating high-performance ultrawide bandgap semiconductor-based bipolar devices. The resulting devices demonstrate exceptional breakdown voltages and efficient thermal management, making them highly suitable for ultra-high-power applications.
Hot News
/
Related to recommend
2025
-
07
-
10
Click on the number of times:
0
Computational Investigations of Metal–Metal Bonding in Molecular Thorium Compounds and Ce and Group IV Analogues来源：ACS PublicationsWe report quantum chemical investigations of metal–metal bonding in m...
2025
-
07
-
09
Click on the number of times:
0
来源：ACS PublicationsThe reaction between isophthalic acid (H2L1) and Gd(NO3)3·6H2O leads to the formation of a two-dimensional (2D) extended framework with the molecular formula [Gd2(L1)3(H2O)2]n ...
2025
-
07
-
08
Click on the number of times:
0
来源：ACS PublicationsA straightforward synthesis of Cp*2Sc(AlMe4) (Cp* = C5Me5) applying Cp*2ScCl(thf) and LiAlMe4/AlMe3 is described. Donor-assisted trimethyltriel exchange gives access to Cp*2Sc(EMe4)...
2025
-
07
-
07
Click on the number of times:
0
Zero-Field Single Molecular Magnet Behavior of Selenotungstate-Encapsulated Dy(III) Tetramers 来源：ACS PublicationsTwo tartaric acid-bridged organic–inorganic hybrid Dy(III)-substituted selenotungs...